Xufeng Luo, Lixiu Zhang, Youxuan Zheng,?, and Liming Ding,?

1State Key Laboratory of Coordination Chemistry, School of Chemistry and Chemical Engineering, Nanjing University, Nanjing 210023, China

2Center for Excellence in Nanoscience (CAS), Key Laboratory of Nanosystem and Hierarchical Fabrication (CAS), National Center for Nanoscience and Technology, Beijing 100190, China

Thermally activated delayed fluorescence (TADF) emitter is a promising organic light-emitting diode (OLED) material due to low cost, wide luminous color gamut and 100% exciton utilization efficiency[1]. To achieve high TADF performance, a feasible strategy is to construct a twisted donoracceptor (D-A) unit, decreasing the overlap between the highest occupied molecular orbital (HOMO) and the lowest unoccupied molecular orbital (LUMO), and minimizing the energy gap (ΔEST) between the lowest singlet (S1) and triplet(T1) states[2,3]. However, this long-range charge transfer feature is often disadvantageous for achieving high oscillator strengths (f) and radiative transition rates (kr)[4](Fig. 1(a)).Moreover, common TADF emitters always display broad electroluminescence spectra, whose full-widths at half-maximum(FWHMs) are 70-100 nm[5]. Therefore, it is necessary to realize a narrow-band emission system, which can improve the display quality greatly, with highkrand high rate constant of reverse intersystem crossing (kRISC).

In 2015, Hetakeymaet al. developed a rigid polycyclic aromatic framework based on B/N system with opposite multiple-resonance (MR) effect for the first time, offering narrowband emission and efficient TADF performance[6](Fig. 1(b)).In the emitter DABNA-1 with a highly rigid framework, the cofacial backbone resulted in short-range charge transfer, giving a high PLQY of 88% and a small FWHM of 30 nm in doped film. The corresponding OLEDs with 1 wt% doping offered a maximum external quantum efficiency (EQEmax) of 13.5% and a FWHM of 28 nm. Through modifying peripheral benzene ring and diphenylamine, the emission peak of DABNA-2 was slightly red-shifted and the OLEDs exhibited a FWHM of 28 nm and an EQEmaxof 20.2%. In terms of device efficiency and color purity, it is superior to previous commercial blue emitters[7], and it also has potential to replace current commercial blue fluorescent materials as the core of OLEDs. Although MR-TADF emitters have achieved nearly full-color emission, this class of materials tends to exhibit poorkRISCvalues(～104s-1) and severe efficiency roll-off at high current densities[8].

The strategies for alleviating the efficiency roll-off in MRTADF OLEDs are as follows: (1) hyperfluorescence sensitization (HFS) by using TADF materials with highkRISC; (2) introducing "heavy atoms" like S or Se into the skeleton; (3) extending charge delocalization by fusing rigid skeleton. In 2019, Adachiet al. designed HFS OLEDs based onν-DABNA[9]and hetero-donor-type TADF material (HDT-1) with accelerated S1energy transfer process[10]. A highkRISC(9.2 × 105s-1) was obtained in doped ternary film. Compared with host-guest type devices, sensitized pure-blue TADF OLEDs showed higher EQE and small efficiency roll-off, and the EQE reached 32% at 1000 cd/m2. Later, Duanet al. fused aza-aromatics into B/N skeleton and synthesized a pure-green AZA-BN emitter (λPL=522 nm, FWHM = 28 nm)[11](Fig. 1(c)). Benefitting from efficient HFS mechanism, HFS OLEDs displayed a higher EQEmaxof 31.6% and smaller efficiency roll-off than non-sensitized devices[12]. Obviously, through the intervention of TADF sensitizer, the ternary emitting layer showed a more efficient triplet-exciton up-conversion rate.

According to Fermi's golden rule, thekRISCin TADF systems mainly depends on spin-orbit coupling (SOC) and energy splitting between S1and T1states, as expressed in equation:kRISC∝ |＜S1|?SOC|T1＞/ΔEST|2[13]. Recently, Yasuda group developed a fused-nonacyclic π-system (BSBS-N1), embedded with B, N, and S atoms. With “heavy atom” S[14], BSBS-N1 exhibited a big ＜S1|?SOC|T1＞ value of 0.31 cm-1and a highkRISCof 1.9 × 105s-1. The corresponding OLEDs offered smaller efficiency roll-off than BBCz-SB LEDs[8]. Similarly, the strategy of using S to improve SOC was further confirmed by Yanget al.[15]kRISCover 105s-1was obtained in toluene solution and MR-TADF OLEDs showed smaller efficiency roll-off.To intuitively reflect the influence of heavy atom on RISC, Yasudaet al. doped Se atom into MR-TADF emitter (CzBSe)[16],yielding a recordkRISCexceeding 108s-1(Fig. 2(a)). Benefitting from its ultrafast triplet-exciton up-conversion, OLEDs with CzBSe offered an EQEmaxof 23.9%, with narrow blue emission (λEL= 481 nm, FWHM = 33 nm) and significantly alleviated efficiency roll-off.

Fig. 1. (Color online) (a) Traditional design strategy for TADF. Reproduced with permission[6], Copyright 2016, Wiley-VCH. (b) Design strategy for MR-TADF. Reproduced with permission[6], Copyright 2016, Wiley-VCH. (c) New MR-TADF skeletons with fused aza-aromatics. Reproduced with permission[11], Copyright 2020, Wiley-VCH.

Extending charge delocalization by fusing rigid skeleton is an effective approach to solve efficiency roll-off of MRTADF OLEDs. By fusing hole-transport units (carbazole, dibenzofuran) into B/N framework, Zhenget al. achieved two π-extended MR-TADF emitters (NBO and NBNP), peaking at 487 and 500 nm with narrow FWHMs of 27 and 29 nm in toluene solutions[17], respectively. ΔESTwere reduced (0.12 eV for NBO, 0.09 eV for NBNP)viacharge delocalization of frontier orbitals. Meanwhile, SOC values were further improved due to the introduction of O and N heteroatoms. As results,kRISCfor NBO and NBNP are nearly an order of magnitude higher than that of BBCz-SB. Consequently, NBO- and NBNP-based OLEDs showed EQEmaxof 26.1% and 28.0%, with low efficiency rolloff. To further enhance the CT state of MR-TADF emitters,Zhenget al. adopted double resonance unit superposition strategy and obtained two green MR-TADF emitters (VTCzBN and TCz-VTCzBN) based on indolo[3,2,1-jk]carbazole (ICz) unit and B/N skeletons[18](Fig. 2(b)), and the emissions peaked at 496 and 521 nm with FWHMs of 34 and 29 nm, respectively.Benefitting from thorough charge delocalization within frontier molecular orbitals, ΔESTvalues were close to 0 eV and large＜S1|?SOC|T1＞ values were obtained. As a result, highkRISCvalues were also achieved, and VTCzBN and TCz-VTCzBN-based OLEDs showed EQEmaxof 31.7% and 32.2%, with low efficiency roll-off, respectively. D-TCz-VTCzBN displayed ultrapure green CIE of (0.22, 0.71), consistent with the green display standard of the National Television System Committee.

Fig. 2. (Color online) (a) Molecular structures of CzBO, CzBS, and CzBSe with different chalcogens, conventional TADF mechanism and ideal superimposed fluorescence (SF) mechanism. Reproduced with permission[16], Copyright 2022, Wiley-VCH. (b) Double resonance unit superposition strategy. Reproduced with permission[18], Copyright 2022, Wiley-VCH.

In short, enhancingkRISCof MR-TADF emitters is crucial for reducing efficiency roll-off of OLEDs. Some strategies are highlighted, like TADF sensitization, heavy atom introduction,extending charge delocalization. More efforts are needed to develop MR-TADF OLEDs with high EQE, low efficiency rolloff and narrow emission.