XIA Qiuying, SUN Shuo, ZAN Feng, XU Jing, XIA Hui

Amorphous LiSiON Thin Film Electrolyte for All-solid-state Thin Film Lithium Battery

XIA Qiuying, SUN Shuo, ZAN Feng, XU Jing, XIA Hui

(School of Materials Science and Engineering, Nanjing University of Science and Technology, Nanjing 210094, China)

All-solid-state thin film lithium battery (TFLB) is regarded as the ideal power source for microelectronic devices. However, the relatively low ionic conductivity of amorphous solid-state electrolyte limits the improvement of electrochemical performance for TFLB. In this work, amorphous lithium silicon oxynitride (LiSiON) thin films are prepared by magnetron sputtering as solid-state electrolyte for TFLB. With optimized deposition condition, the LiSiON thin film exhibits a high ionic conductivity of 6.3×10–6S?cm–1at room temperature and a wide voltage window over 5 V, making it a suitable thin film electrolyte for TFLB. A MoO3/LiSiON/Li TFLB is constructed based on the LiSiON thin film electrolyte with large specific capacity (282 mAh?g–1at 50 mA?g–1), good rate capability (50 mAh?g–1at 800 mA?g–1), and acceptable cycle life (78.1% capacity retention after 200 cycles), demonstrating the feasibility of this electrolyte for practical applications.

LiSiON; thin film electrolyte; all-solid-state lithium battery;thin film battery

The rapid development of microelectronics industry, such as micro-electromechanical systems (MEMS), micro sensors, intelligent cards, and implantable micro medical devices, leads to increasing demands for inte-grated micro-sized energy storage[1-2].Among the avai-lable battery technologies, all-solid-state thin film lith-ium battery (TFLB) is considered as the ideal power source for microelectronic devices due to their high safety, small size, power-on-chip design, long cycle life, and low self-discharge rate. As one of the key com-ponents in TFLB, solid-state thin film electrolyte plays a vital role in determining the properties of TFLB[3]. Therefore, developing high-performance solid-state thin film ele-ctrolyte is always an important goal for the development of TFLB. At present, the most widely used electrolyte in TFLB is amorphous lithium phosphorus oxynitride (LiPON), which has moderate ionic condu-ctivity (2×10–6S?cm–1), low electronic conductivity (～10–14S?cm–1), wide voltage window (～5.5 V), and good contact stability with lithium[4-5]. However, its ionic conductivity is relatively low, which impedes the future development of high power TFLB for the upcoming era of the Internet of Things (IoT)[6].Thus, it is urgent to develop new thin film electrolytes with increased ionic conductivity, as well as large voltage window and good contact stability with lithium for next-generation TFLB.

Among various inorganic solid-state electrolyte materials, the Li2O-SiO2solid solution system and their deuterogenic phases were identified as potential thin film electrolytes due to their fast three-dimensional lithium conduction channels[7]. For example, Chen,.[8]reported that Al substituted Li4.4Al0.4Si0.6O4-0.3Li2O solid electrolyte has a high ionic conductivity of 5.4×10–3S?cm–1at 200 ℃. Adnan,.[9]found that Li4Sn0.02Si0.98O4compound possesses a maximum conductivity value of 3.07×10?5S?cm?1at ambient temperature. However, previous works on Li2O-SiO2electrolyte systems mostly focused on powder materials with high crystallinity, while very limited work was reported on their amorphous thin film counterparts for TFLB. Since TFLB is typically constructed by depositing thin films of cathode, electrolyte and anode layer by layer, the electrolyte film is required to be prepared at relatively low temperature to avoid the unfavorable interactions between the cathode and electrolyte, which result in crack and short circuit of the TFLB[1-2]. Thus, developing Li2O-SiO2electrolyte with amorphous feature prepared at low temperature is important for TFLB. Although recent work[6]shows that a high lithium ionic conductivity of 2.06×10?5S?cm–1can be obtained by amorphous Li-Si-P-O-N thin film, its contact stability with the electrodes and electrochemical stability in TFLB have yet to be investigated. Therefore, it is critically important to develop high-performance Li2O-SiO2based thin film electrolyte and demonstrate its actual app-lication in TFLB.

In this work, amorphous lithium silicon oxynitride (LiSiON) thin film was prepared by radio frequency (RF) magnetron sputtering at room temperature and inve-stigated as solid-state electrolyte for TFLB. The sput-tering power and the flow of N2/Ar working gas were optimized to obtain the best deposition condition for the LiSiON thin film. Moreover, to demonstrate the app-licability of the optimized LiSiON electrolyte for TFLB, a MoO3/LiSiON/Li full cell was constructed and its ele-ctrochemical performance was systematically investigated.

1 Experimental

1.1 Preparation of LiSiON thin films

LiSiON thin films were prepared by RF magnetron sputtering (Kurt J. Lesker) using a Li2SiO3target (76.2 mm in diameter) at room temperature for 12 h. Before deposition, the pressure of the chamber was reduced to less than 1×10?5Pa. The distance from target to substrate was 10 cm. The samples deposited under RF power of80, 100, and 120 W at the flow of 90 sccm N2are marked as sample LiSiON-80N9, LiSiON-100N9, and LiSiON-120N9, respectively. And the samples de-posited under RF power of100 W at the flow of90 sccm N2and 10 sccm Ar, 90 sccm N2and 50 sccm Ar, 50 sccm N2and 50 sccm Ar are marked as sample LiSiON- 100N9A1, LiSiON-100N9A5, and LiSiON-100N5A5, respectively.

1.2 Preparation of MoO3/LiSiON/Li TFLB

MoO3film was prepared by direct current (DC) reactive magnetron sputtering (Kurt J. Lesker) using a pure metal Mo target (76.2 mm in diameter) according to our previous report[10]. The distance from target to substrate was 10 cm, and DC sputtering power was 60 W. The deposition was performed at the substrate temper-ature of 100 ℃ for 4 h at the flow of 40 sccm Ar and 10 sccm O2, followed by anannealing treatment at 450 ℃ for 1 h. LiSiON-100N9A1 was then deposited on the MoO3film as electrolyte. After that, a metallic lithium film of about 2 μm in thickness was deposited on the LiSiON film by vacuum thermal evaporation (Kurt J. Lesker). The final fabrication step involved the depo-sition of Cu current collector and the encapsulation process.

1.3 Material characterization

The crystal structures of the samples were chara-cterized by X-ray diffraction (XRD, Bruker D8 Advance). The morphologies and microstructures of the samples were characterized by field emission scanning electron microscope (FESEM, FEI Quanta 250F) equip-ped with energy-dispersive X-ray spectroscopy (EDS). The ele-mental compositions of the samples were ana-lyzed by inductively coupled plasma mass spectrometry (ICP-MS, Agilent 7700X). The chemical composition and bonding information of the samples were measured by X-ray photoelectron spectroscopy (XPS, Escalab 250XI, Ther-mo Scientific).

1.4 Electrochemical measurements

The ionic conductivity of the LiSiON thin film electrolyte was measured using a sandwiched structure of Pt/LiSiON/Pt. The electrochemical impedance spectro-scopy (EIS) (from 1000 kHz to 0.1 Hz with potential amplitude of 5 mV) and cyclic voltammetry (CV) measurements of the samples were carried out on the Biologic VMP3 electrochemical workstation. Galvano-static charge/discharge (GCD) measurement of the MoO3/LiSiON/Li TFLB was carried out using a Neware BTS4000 battery system in an argon-filled glove box at room temperature. A Sartorius Analytical Balance (CPA225D, with resolution of 10 μg) was used to determine the electrode mass loading, and the mass loading of the MoO3film is about 0.4 mg?cm–2.

2 Results and discussion

As shown in the optical image inserted in Fig. 1(a), a Li2SiO3target was employed to prepare LiSiON thin film. The XRD result in Fig. 1(a) reveals that the target is composed of the major Li2SiO3(JCPDS 83-1517) phase and minor SiO2phase. ICP-MS measurement indicates that the atomic ratio of Li : Si is about 1.79 : 1 in the target. Transparent amorphous thin film was obtained for the typical sample LiSiON-100N9A1 after sputtering the target (Fig. 1(b)). The thickness of the typical sample LiSiON-100N9A1 measured from the cross-section FESEM image in Fig. 1(c) is about 1.2 μm, indicating a growth rate of about 100 nm?h–1under this condition. As shown in the top-view FESEM image in Fig. 1(d), the surface of the LiSiON thin film is very smooth and dense without cracks or pinholes, making it a suitable solid electrolyte for TFLB to avoid shortcut and safety problem.

XPS analysis was carried out to investigate the chemical composition and bonding information of the Li2SiO3target and typical sample LiSiON-100N9A1. The XPS survey scan spectra in Fig. 2(a) reveal the presence of Li, Si, and O elements in the Li2SiO3target and the introduction of N element in the LiSiON thin film. The atomic ratio of N : Si in LiSiON thin film is about 0.33 : 1 according to the XPS result. Combining with the corresponding atomic ratio (1.51 : 1) obtained by the ICP-MS measurement, the stoichiometry of the typical sample LiSiON-100N9A1 is determined to be Li1.51SiO2.26N0.33. Compared with the single Si–Si (103.2 eV) peak in the Si2p core-level XPS spectrum of the Li2SiO3target (Fig. 2(b)), additional Si–N (101.6 eV) peak can be observed from the LiSiON thin film, suggesting the occurrence of nitridation in LiSiON[11-12]. The O1s core-level XPS spectrum of Li2SiO3target in Fig. 2(c) shows two bonding environments: 531.5 eV originated from SiOand 528.8 eV assigned to Li2O. After deposition, additional component emerged at 530.2 eV can be observed with LiSiON thin film, which can be assigned to nonbridging oxygen (On) in sili-cate[13-14]. The N1s core-level XPS spectrum of LiSiON thin film in Fig. 2(d) can be deconvoluted into three peaks, including 398.2 eV for Si–N bonding, 396.4 eV for Li3N, and 403.8 eV for nitrite species NO2–, further confirming the incorporation of N into the LiSiON network[14-16]. As schematically illustrated in Fig. 2(e), the incorporation of N into the LiSiON network can form more cross-linked structure, which is beneficial for fast lithium ion conduction[6,17].

To optimize the ionic conductivity and electroche-mical stability of the LiSiON thin films, various LiSiON thin films deposited at different sputtering powers, and working gas flows were compared in terms of their ionic conductivities and voltage windows. The room-temper-ature Nyquist plots of the LiSiON thin films are depicted in Fig. 3(a), and the corresponding Pt/LiSiON/Pt sandwich structure and equivalent circuit are shown in Fig. 3(b). As observed, the Nyquist plots exhibit a single semicircle and dielectric capacitance tail, which is characteristic of thin-film conducting dielectric with bulk relaxation process sandwiched between blocking con-tacts[17]. The ionic conductivities (i) of the LiSiON thin films can be calculated by using Eq. (1).

i=/() (1)

whereis the film thickness,is the effective area (about 1 cm2), andis the film resistance estimated from the measured Nyquist plot. The calculated ionic conductivities for these LiSiON thin films are compared in Table 1. As observed, the ionic conductivity of the LiSiON thin film deposited at a constant flow of 90 sccm N2increases with the increasing sputtering power from 80 W to 100 W, then decreases when the sputtering power is further elevated to 120 W, which is similar to previous report on LiPON electrolyte[18]. An obvious increment in the ionic conductivities can be observed when the N2ratio in the working gas under a constant sputtering power of 100 W is promoted, which can be attributed to the increased amount of incorporated nitrogen in the LiSiON with more favorable environment for lithium ion motion[5, 18]. Noticeably, the sample LiSiON- 100N9 and LiSiON-100N9A1 show the highest ionic conductivities of 7.1×10?6and 6.3×10?6S?cm–1, respe-ctively, which are obviously higher than the well-known LiPON (～2×10?6S?cm–1), previous reported amorphous LiNbO3(～1×10–6S?cm–1)[19], LiBON (2.3×10–6S?cm–1)[20], Li-V-Si-O (～1×10–6S?cm–1)[21], Li-La-Zr-O (4×10–7S?cm–1)[22], and Li-Si-P-O (1.6×10–6S?cm–1)[23]electrolyte films, revealing that the amorphous LiSiON thin film is a competitive candidate as electrolyte for TFLB. The high ion conductivity of the LiSiON thin film can be attributed to the incorporation of N into the thin film and the formation of Si?N bonds instead of Si?O bonds, leading to a more reticulated anionic network for the facile lithium ion mobility[17, 24]. The electrochemical stable voltage windows of the LiSiON thin films were evaluated by CV measurement at a scan rate of 5 mV?s–1with voltage up to 5.5 V. It should be pointed out that the impact of deposition condition on the voltage window of LiSiON films varies, which cannot be explained by a clear mechanism currently since there are no relevant researches in previous reports about thin film electro-lyte[18,24-25]. Nevertheless, as compared in Fig. 3(c) and Table 1, the sample LiSiON-100N9A1 and LiSiON- 100N5A5 show the broadest voltage windows of ～5.0 and ～5.2 V, respectively, which are close to that of LiPON electrolyte. Therefore, taken both the ionic conductivity and voltage window into consideration, sample LiSiON- 100N9A1 was chosen for further inve-stigation and the fabrication of full cell. To explore the lithium ion transference number (i) and the electronic conductivity (e) of sample LiSiON-100N9A1, chrono-amperometry was further performed at a constant voltage of 10 mV (Fig. 3(d)). Theican be calculated by Eq. (2).

Fig. 2 (a) Survey-scan, (b) Si2p core-level, (c) O1s core-level, and (d) N1s core-level XPS spectra of Li2SiO3 target and typical sample LiSiON-100N9A1; (e) Schematic illustration of the partial structure change from Li2SiO3 to LiSiON with the incorporation of N

Fig. 3 (a) Electrochemical impedance spectroscopy (EIS) spectra of the LiSiON thin films deposited under different conditions; (b) Schematic illustration of the Pt/LiSiON/Pt sandwich structure and the corresponding equivalent circuit; (c) CV curves of the LiSiON thin films deposited under different conditions; (d) Chronoamperometry curve of the sample LiSiON-100N9A1

Table 1 Comparison of lithium ion conductivities and voltage windows of LiSiON thin films deposited underdifferent conditions

i=(b–e)/b(2)

wherebis the initial polarization current, andeis the steady state current[18]. Theiwas calculated to be 0.998, which is close to 1, indicating that the lithium ions conduction is absolutely dominant in the electrolyte. Theiis determined by a mixed effect of the conduction of ions and electrons[24], which can be expressed by Eq. (3).

i=i/(i+e) (3)

Thus, theeof the sample LiSiON-100N9A1 is calcu-lated to be 1.26×10?8S?cm–1, which is negligible compared to its ion conductivity.

To verify the feasibility of the optimized sample LiSiON- 100N9A1 for TFLB application, MoO3/LiSiON/Li TFLB was further fabricated. The cross-section FESEM image and corresponding EDS mapping images of the MoO3/LiSiON/Li TFLB are shown in Fig. 4(a). As observed, the MoO3cathode (about 1.1 μm in thickness) and the Li anode are well separated by the LiSiON electrolyte, and the LiSiON electrolyte has tight contact interfaces with both the cathode and the anode. Fig. 4(b) displays the typical CV curve of the TFLB at a scan rate of 0.1 mV?s?1between 1.5–3.5 V, which shows a pair of well-defined redox peaks at around 2.25 and 2.65 V, corresponding to lithium ion insertion into and extraction from the MoO3[10]. Fig. 4(c) depicts the initial 3 galva-nostatic charge/discharge curves of the TFLB at a current density of 50 mA?g–1(20 μA?cm–2, based on the mass of MoO3film). As observed, the TFLB delivers the initial charge/discharge capacities of 145/297 mAh?g–1(58/118.8 μAh?cm–2). After the 2nd cycle, steady cycling behavior with high reversible specific capacity of 282 mAh?g–1was achieved by the TFLB. The rate performance of the TFLB at various current densities is depicted in Fig. 4(d). The irreversible capacity loss of the TFLB in initial several cycles at low current density can be attributed to irreversible phase transition in the MoO3derived by lithium insertion[26]. Stable discharge capa-cities of about 219, 173, 107, and 50 mAh?g–1are observed at 100, 200, 400, and 800 mA?g–1, respectively, demonstrating good rate capability. To evaluate the electrochemical stability of the TFLB, cycle performance was further performed at a current density of 200 mA?g–1(Fig. 4(e)). The TFLB can retain 78.1% of its initial discharge capacity after 200 cycles, and the Coulombic efficiency is near 100% for each cycle, revealing acce-ptable electrochemical stability of the LiSiON electrolyte. EIS measurements were further carried out at open circuit voltage to investigate the electrolyte/electrode interface in the TFLB at different cycle numbers, and the corresponding Nyquist plots with equivalent circuit are depicted in Fig. 4(f). As observed, the MoO3/LiSiON/Li TFLB shows similar EIS spectrum which consists of two semicircles in the high frequency region at fresh state to that of the MoO3/LiPON/Li TFLB in our previous work[10], indicating that the Li/LiSiON interfacial resistance is negligible compared to that of the LiSiON/MoO3interface[20]. The first small semicircle in the Nyquist plots is attributed to the ionic conduction of Li+ions in LiSiON electrolyte, while the second large semicircle corresponds to the charge transfer process at the LiSiON/MoO3interface[27-28]. It is noted that the first small semicircle rarely changes during the cycles, indicating the relatively good cyclic stability of the LiSiON electrolyte. However, the second semicircle gradually expands as the cycle number evolves, revealing the increased LiSiON/MoO3interfacial resistance during cycling, which could be the main reason for the capacity fading of the TFLB[29]. It is worth mentioning that this work successfully adopts the LiSiON electrolyte to construct TFLB and demonstrates the good interfacial contact of LiSiON with both the MoO3cathode and the lithium anode for the first time. Moreover, the large specific capacity, good rate capability, and acceptable cycle performance of the MoO3/LiSiON/Li TFLB demonstrate that the LiSiON thin film is well applicable as electrolyte for TFLB.

Fig. 4 (a) Cross-section FESEM image and corresponding EDS mapping images of the MoO3/LiSiON/Li TFLB; (b) Typical CV curve, (c) initial three charge/discharge curves, (d) rate performance, (e) cycle performance, and (f) EIS spectra at different cycle numbers of the MoO3/LiSiON/Li TFLB with sample LiSiON-100N9A1 as electrolyte

3 Conclusions

In summary, amorphous LiSiON thin film electrolyte was successfully prepared by RF magnetron sputtering using Li2SiO3target with N2/Ar gas flow. The optimized LiSiON thin film deposited under RF power of 100 W at the flow of 90 sccm N2and 10 sccm Ar possesses smooth surface, dense structure, high ion conductivity (6.3×10?6S?cm?1), and wide voltage window (5 V), making it a promising electrolyte material for TFLB. More impor-tantly, by using the LiSiON electrolyte, a MoO3/LiSiON/Li TFLB was successfully demonstrated for the first time with high specific capacity (282 mAh?g–1at 50 mA?g–1), good rate performance (50 mAh?g–1at 800 mA?g–1), and acceptable cycle stability (78.1% capa-city retention after 200 cycles). This work is exp-ected to bring new opportunities to develop high- performance TFLB by using Li2O-SiO2based thin film electrolyte.

[1] MOITZHEIM S, PUT B, VEREECKEN P M. Advances in 3D thin-film Li-ion batteries., 2019, 6(15): 1900805.

[2] XIA Q, ZHANG Q, SUN S,. Tunnel intergrowth LiMnO2nanosheet arrays as 3D cathode for high-performance all-solid- state thin film lithium microbatteries., 2021, 33(5): 2003524.

[3] DENG Y, EAMES C, FLEUTOT B,. Enhancing the lithium ion conductivity in lithium superionic conductor (LISICON) solid electrolytes through a mixed polyanion effect., 2017, 9(8): 7050–7058.

[4] BATES J B, DUDNEY N J, GRUZALSKI G R,. Fabrication and characterization of amorphous lithium electrolyte thin films and rechargeable thin-film batteries., 1993, 43(1/2/3): 103–110.

[5] BATES J. Electrical properties of amorphous lithium electrolyte thin films., 1992, 53(56): 647–654.

[6] FAMPRIKIS T, GALIPAUD J, CLEMENS O,. Composition dependence of ionic conductivity in LiSiPO(N) thin-film electrolytes for solid-state batteries., 2019, 2(7): 4782–4791.

[7] DENG Y, EAMES C, CHOTARD J N,. Structural and mechanistic insights into fast lithium-ion conduction in Li4SiO4- Li3PO4solid electrolytes., 2015, 137(28): 9136–9145.

[8] CHEN R, SONG X. The ionic conductivity of solid electrolytes for Li4+xMSi1–xO4–yLi2O (M=Al, B) systems., 2002, 49: 7–10.

[9] ADNAN S, MOHAMED N S. Effects of Sn substitution on the properties of Li4SiO4ceramic electrolyte., 2014, 262: 559–562.

[10] SUN S, XIA Q, LIU J,. Self-standing oxygen-deficient-MoO3–xnanoflake arrays as 3D cathode for advanced all-solid- state thin film lithium batteries., 2019, 5(2): 229–236.

[11] DING W, LU W, DENG X,. An XPS study on the structure of SiNfilm deposited by microwave ECR magnetron sputtering., 2009, 58(6): 4109–4116.

[12] KIM H, KIM Y. Partial nitridation of Li4SiO4and ionic conductivity of Li4.1SiO3.9N0.1., 2018, 44(8): 9058–9062.

[13] MARIKO M, HIDEMASA K ,TOMOYUKI O,. Analysis of SiO anodes for lithium-ion batteries.,2005, 152(10): A2089.

[14] FINGERLE M, BUCHHEIT R, SICOLO S,. Reaction and space charge layer formation at the LiCoO2-LiPON interface: insights on defect formation and ion energy level alignment by a combined surface science–simulation approach., 2017, 29(18): 7675–7685.

[15] WEST W, HOOD Z, ADHIKARI S,. Reduction of charge- transfer resistance at the solid electrolyte-electrode interface by pulsed laser deposition of films from a crystalline Li2PO2N source., 2016, 312: 116–122.

[16] SICOLO S, FINGERLE M, HAUSBRAND R,. Interfacial instability of amorphous LiPON against lithium: a combined density functional theory and spectroscopic study., 2017, 354: 124–133.

[17] WU F, LIU Y, CHEN R,. Preparation and performance of novel Li-Ti-Si-P-O-N thin-film electrolyte for thin-film lithium batteries., 2009, 189(1): 467–470.

[18] PUT B, VEREECKEN M, MEERSSCHAUT J,. Electrical characterization of ultrathin RF-sputtered LiPON layers for nanoscale batteries.,2016, 8(11): 7060?7069.

[19] NIINOMI H, MOTOYAMA M, IRIYAMA Y. Li+Conduction in Li-Nb-O films deposited by a Sol–Gel method., 2016, 285: 13–18.

[20] SONG S, LEE K, PARK H. High-performance flexible all-solid-state microbatteries based on solid electrolyte of lithium boron oxynitride., 2016, 328: 311–317.

[21] OHTSUKA H, OKADA S, YAMAKI J. Solid state battery with Li2O-V2O5-SiO2solid electrolyte thin film., 1990, 40–41: 964–966.

[22] Kalita D, Lee S, Lee K,. Ionic conductivity properties of amorphous Li-La-Zr-O solid electrolyte for thin film batteries., 2012, 229: 14–19.

[23] SAKURAI Y, SAKUDA A, HAYASHI A,. Preparation of amorphous Li4SiO4-Li3PO4thin films by pulsed laser deposition for all-solid-state lithium secondary batteries., 2011, 182: 59–63.

[24] TAN G, WU F, LI L,. Magnetron sputtering preparation of nitrogen-incorporated lithium-aluminum-titanium phosphate based thin film electrolytes for all-solid-state lithium ion batteries., 2012, 116(5): 3817–3826.

[25] YU X, BATES J B, JELLISON G,. A stable thin-film lithium electrolyte: lithium phosphorus oxynitride., 1997, 144(2): 524.

[26] KIM H, COOK J, LIN H,. Oxygen vacancies enhance pseudocapacitive charge storage properties of MoO3–x., 2017, 16: 454–460.

[27] SONG H, WANG S, SONG X,. Solar-driven all-solid-state lithium-air batteries operating at extreme low temperatures.,2020, 13(4): 1205–1211.

[28] WANG Z, LEE J, XIN H,. Effects of cathode electrolyte interfacial (CEI) layer on long term cycling of all-solid-state thin-film batteries., 2016, 324: 342–348.

[29] QIAO Y, DENG H, HE P,A 500 Wh/kg lithium-metal cell based on anionic redox., 2020, 4(6): 1311–1323.

非晶LiSiON薄膜電解質(zhì)的全固態(tài)薄膜鋰電池性能

夏求應(yīng), 孫碩, 昝峰, 徐璟, 夏暉

(南京理工大學(xué) 材料科學(xué)與工程學(xué)院, 南京 210094)

全固態(tài)薄膜鋰電池(TFLB)是理想的微電子系統(tǒng)電源。目前報(bào)道的固態(tài)非晶電解質(zhì)存在離子電導(dǎo)率偏低的問(wèn)題, 限制了TFLB性能的提升。本工作采用磁控濺射法制備了一種新型非晶鋰硅氧氮(LiSiON)薄膜用作TFLB的固態(tài)電解質(zhì)。結(jié)果表明, 優(yōu)化制備條件后的LiSiON薄膜具有6.3×10–6S?cm–1的高離子電導(dǎo)率以及超過(guò)5 V的寬電壓窗口, 適合作為T(mén)FLB的電解質(zhì)。在LiSiON薄膜電解質(zhì)的基礎(chǔ)上, 本工作構(gòu)建了MoO3/LiSiON/Li TFLB并獲得高的比容量(50 mA?g–1下282 mAh?g–1)、良好的倍率性能(800 mA?g–1下50 mAh?g–1)和可觀的循環(huán)壽命(200次循環(huán)后容量保持率為78.1%), 驗(yàn)證了該電解質(zhì)在薄膜電池中應(yīng)用的可行性。

LiSiON; 薄膜電解質(zhì); 全固態(tài)鋰電池; 薄膜電池

TQ174

A

2021-03-06;

2021-05-06;

2021-06-10

National Key R&D Program of China (2020YFB2007400); National Natural Science Foundation of China (51802159, 51972174, 52002183)

XIA Qiuying (1991–), male, PhD. E-mail: qiuyingxia@njust.edu.cn

夏求應(yīng)(1991–), 男, 博士. E-mail: qiuyingxia@njust.edu.cn

XIA Hui, professor. E-mail: xiahui@njust.edu.cn

夏暉, 教授. E-mail: xiahui@njust.edu.cn

1000-324X(2022)02-0230-07

10.15541/jim20210132